En 3D-printerresin, der har lav krympning og korte hærdetider. Det er både holdbart og nemt at printe og kan males med almindeligt anvendte malinger. Perfekt til meget detaljerede udstillingsmodeller.
- Beholder: flaske
- Nettovægt: 500 ml ± 5 %
- Bølgelængde: 405 nm
Ikke på lager
23659
Skriv din e-mail-adresse her, hvis du vil have besked når vi igen har denne vare på lager:
Jeg ønsker en e-mail når varen kommer på lager
Precise and Safe
A 3D printing resin that has low shrinkage and short curing times. It's both durable and easy to print and can be painted with commonly-used paints. Perfect for highly-detailed exhibition models.
- Container: Bottle
- Net weight: 500 ml ± 5%
- Wavelength: 405 nm
Epoxy-based Resin for 3D Printing
Zortrax Resin BASIC is an epoxy-based resin offering sharp edges, high detail, and short curing times. It’s durable and easy to print. It’s available in grey, white, and pigment free. Zortrax Resin BASIC contains no volatile organic compounds, so it is safe to print with when used in accordance with our safety instructions. The already cured resin is easy to paint.
This resin has very low shrinkage. Its shore hardness is 82.2 D for the pigment-free version and as high as 88 D for ivory and grey versions. Due to its composition, Zortrax Resin BASIC offers smooth surfaces. It can be cured with UV light with 405 nm wavelength.
Main Features:
- Low shrinkage
- Easy of painting
- Safe for health and environment
Applications
- Casings for electronics
- Functional prototypes
- Exhibition models
- End-use parts
- Translucent models (pigment free only)
| Mærke | Zortrax |
| Farve | Hvid |
| Dedicated for | Container | Netto Weight | Wavelenght | |
|---|---|---|---|---|
| Zortrax Inkspire | bottle | 500 ml ± 5% | 405 nm | |
| White/Ivory; Grey | Pigment-free | |||
| Mechanical Properties | Metric | Imperial | Metric | Imperial |
| Tensile strength | 36 -52 MPa | 5220 - 7540 psi | 35.7 MPa | 5180 psi |
| Tensile Modulus | 1.779 - 2.385 GPa | 258 - 346 ksi | - | - |
| Elongation at Break | 11 - 20% | 11 - 20% | 3% | 3% |
| Flexural Strength | 59 - 70 MPa | 8560 - 10200 psi | - | - |
| Flexural Modulus | 1.882 - 2.385 GPa | 273 - 346 ksi | 1.56 GPa | 226 ksi |
| Izod Impact, Notched | 44 - 49 J/m | 0.824 - 0.918 ft-lb/in | - | - |
| Other Properties | Metric | Imperial | Metric | Imperial |
| Viscosity | 150 - 200 mPa*s | 0.00313 - 0.00418 lbf-s/ft2 | 33 - 57 mPa*s | 0.000689 - 0.00119 lbf-s/ft2 |
| Density | 1.05 - 1.13 g | 0.00232 - 0.00249 lb | - | - |
| Shrinkage | 3.72 - 4.24% | 3.72 - 4.24% | 2% +/- 1% | 2% +/- 1% |
| Shore Hardness (D) | 88 | 88 | 82.2 | 82.2 |
| Glass Transition Temperature | 100° C | 212° F | - | - |
| Hot Deformation Temperature | 80° C | 176° F | - | - |