Copper3D PLActive - 1.75 mm - 750 g - Apple Green

Copper3D Copper3D

25079

PLACTIVE AN1 ™ er en innovativ Nanocomposite udviklet med en høj kvalitet PLA og et patenteret, videnskabeligt valideret og meget effektivt Nano-Copper additiv.

Flere detaljer

På lager

625,00 DKK

inkl. moms

Køb for 750,00 DKK mere for at få fri fragt

PLACTIVE AN1™ is an innovative Nanocomposite developed with a high quality PLA and a patented, scientifically validated and highly effective Nano-Copper additive. This unique combination of technologies brings the following characteristics to our products:

Antibacterial action has been scientifically validated eliminating more than 99.99% of fungi, viruses, bacteria and a wide range of microorganisms.

Antibacterial properties confirmed by two microbiology laboratories in Chile and USA.
PLACTIVE™ is a FDA Registered Material and EU compliant (No. 10/2011, No. 1935/2004 and No. 2023/2006).
The manufacturer also has certification ISO 9001/2015 and is REACH compliant.

It has thermoforming characteristics that facilitates post-processing and final adjustments of the 3D printed application.

Clinically tested in prosthesis for amputees with excellent results. Ideal for the manufacture of other medical applications where it’s dangerous to have bacterial contamination, such as postoperative prostheses, wound dressing and surgical equipment

The Nano-Additive mantains all the mechanical properties of the material.

PLACTIVE is currently being tested by NASA to evaluate its impact on interplanetary microbial contamination.

Non-toxic product and environmentally friendly (biodegradable).

PLACTIVE ™ ANTIBACTERIAL ACTIVITY

This graphic shows the results of 2 studies conducted by microbiology laboratories in USA and Chile1,2. Both studies confirm that the Colony Forming Units (CFU) of Staphylococcus aureus MRSA and Escherichia coli DH5α, falls abruptly during the first 6 hours of exposure to PLACTIVE (>95%), continuing the elimination of bacterial strains until reaching >98% elimination at 8 hours and >99.99% elimination at 24 hours.

1. SITU Biosciences Microbiology Laboratory, USA.
2. Microbiology Laboratory of Universidad Católica de Valparaíso, Chile.

Copper3D

Mærke Copper3D
Materiale PLA
Diameter 1.75mm
Farve Grøn
Vægt 750g
Print temperatur 190°C - 210°C
Opvarmet seng krævet Nej
Anbefalet temperatur på seng 0°C - 60°C
Lager Online

3D PRINTER CONFIGURATION PARAMETERS WITH PLACTIVE ™

PRINTING TEMP. 190 - 210 °C
PRINTING SPEED 40 - 50 MM/SEG
LAYER HEIGHT ≥ 0.1 MM
PRINT BED TEMP. ± 0 - 60 °C

MATERIAL PROPERTIES OF PLACTIVE ™

Physical Properties PLACTIVE ™ ASIM Method
Specific Gravity, g/cc 1.24 D792
MFR, g/10 min(2) 6 D1238
Relative Viscosity(3) 4.0 D5225
Clarity Transparent  
Peak Melt Temperature, °C 145-160 D3418
Glass Transition Temperature, °C 55-60 D3418
Mechanical Property    
Tensile Yield Strength, psi (MPa) 8700 (60) D882
Tensile Strength at Break, psi (MPa) 7700 (53) D882
Tensile Modulus, psi (MPa) 524,000 (3.6) D882
Tensile Elongation, % 6 D882
Notched Izod Impact, ft-lb/in (J/m) 0.3 (16) D256
Flexural Strength, psi (MPa) 12,000 (83) D790
Flexural Modulus, psi (MPa) 555,000 (3.8) D790
Heat Distortion Temperature, °C
66 psi (0.45 MPa)
55 E2092

“Keep the package sealed until ready to use and promptly reseal any unused material”
(1) Typical properties for injection molded amorphous bars; not to be construed as specifications.
(2) 210 °C/2. 16kg
(3) RV measured at 1.0 g/dL in chicroform at 30°C
*values can vary by +/- 5% due to environmental conditions

3D PRINTER CONFIGURATION PARAMETERS WITH PLACTIVE ™

PRINTING TEMP. 190 - 210 °C
PRINTING SPEED 40 - 50 MM/SEG
LAYER HEIGHT ≥ 0.1 MM
PRINT BED TEMP. ± 0 - 60 °C

MATERIAL PROPERTIES OF PLACTIVE ™

Physical Properties PLACTIVE ™ ASIM Method
Specific Gravity, g/cc 1.24 D792
MFR, g/10 min(2) 6 D1238
Relative Viscosity(3) 4.0 D5225
Clarity Transparent  
Peak Melt Temperature, °C 145-160 D3418
Glass Transition Temperature, °C 55-60 D3418
Mechanical Property    
Tensile Yield Strength, psi (MPa) 8700 (60) D882
Tensile Strength at Break, psi (MPa) 7700 (53) D882
Tensile Modulus, psi (MPa) 524,000 (3.6) D882
Tensile Elongation, % 6 D882
Notched Izod Impact, ft-lb/in (J/m) 0.3 (16) D256
Flexural Strength, psi (MPa) 12,000 (83) D790
Flexural Modulus, psi (MPa) 555,000 (3.8) D790
Heat Distortion Temperature, °C
66 psi (0.45 MPa)
55 E2092

“Keep the package sealed until ready to use and promptly reseal any unused material”
(1) Typical properties for injection molded amorphous bars; not to be construed as specifications.
(2) 210 °C/2. 16kg
(3) RV measured at 1.0 g/dL in chicroform at 30°C
*values can vary by +/- 5% due to environmental conditions

Der er ingen kundeanmeldelser endnu.

Skriv en anmeldelse

Copper3D PLActive - 1.75 mm - 750 g - Apple Green

Copper3D PLActive - 1.75 mm - 750 g - Apple Green

Acceptér Cookie deklaration på Solunoid.dk Websitet anvender cookies til at huske dine indstillinger, statistik og målrette annoncer. Denne information deles med tredjepart.       LÆS MERE